Grade : 304L
Types: Stainless Steel Sheet
00Cr19Ni10 Corrosion resistance, heat resistance, low temperature strength and mechanical properties; good hot workability such as stamping and bending, no heat treatment hardening.

Analysis of 304L stainless steel chemical composition%

Carbon C: ≤ 0.03,Silicon Si: ≤1.0,Manganese Mn: ≤2.0,Chromium Cr: 18.0~20.0,

Nickel Ni: 9.0 to 12.0,Sulfur S: ≤0.03Phosphorus P : ≤ 0.045;

Mechanical properties
Mechanical properties of 304L stainless steel:
Yield strength (N/mm2) ≥ 205,Tensile strength ≥520,Elongation (%) ≥ 40,Hardness HB ≤187,HRB≤90 HV ≤200

Stainless steel rod
Density 7.93 g·cm-3,Specific heat c (20 ° C) 0.502 J · (g · C) -1

Thermal conductivity λ/W(m·°C)-1 (at the following temperature/°C)
20 100 500
12.1 16.3 21.4
Linear expansion coefficient α / (10-6 / ° C) (between the following temperatures / ° C)
20～100 20～200 20～300 20～400
16.0 16.8 17.5 18.1   ,Resistivity 0.73 Ω·mm2·m-1   ,Melting point 1398～1420°C